山特維克藥芯焊絲
|
品名
|
類別
|
AWS型號
|
化學成分（名義值）
|
|
C
|
Si
|
Mn
|
Pmax
|
Smax
|
Cr
|
Ni
|
Mo
|
|
藥芯焊絲
|
19.9.LT
|
308LT1-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.025
|
19.5
|
10
|
|
|
19.9.LVT
|
308LT1-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.03
|
19.5
|
10
|
|
|
19.9.NbT
|
347T1-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.025
|
19.5
|
10
|
|
|
19.12.3.LT
|
316LT1-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.025
|
18.5
|
12.5
|
2.7
|
|
19.12.3.LVT
|
316LT1-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.03
|
18.5
|
12.5
|
2.7
|
|
24.13.LT
|
309LT1-4
|
0.030
|
0.5
|
1.0
|
0.03
|
0.025
|
23.5
|
13
|
|
|
24.13.LVT
|
309LT1-4
|
0.030
|
0.5
|
1.0
|
0.03
|
0.03
|
23.5
|
13
|
|
|
22.15.3.LT
|
309LmoT1-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.03
|
23
|
13
|
3.0
|
|
29.9.T
|
312T1-4
|
0.15
|
0.6
|
1.7
|
0.03
|
0.03
|
29
|
9.5
|
|
|
22.9.3.LT
|
2209T0-4
|
0.030
|
0.5
|
1.5
|
0.03
|
0.03
|
23
|
9.5
|
3.1
|
|
22.12.HTT
|
|
0.10
|
0.7
|
0.9
|
0.025
|
0.025
|
22
|
11
|
|
鎳及鎳合金焊條的選用和使用
（1）鎳及鎳合金焊條的選用原則 鎳及鎳合金焊條主要根據被焊母材的合**號、化學成分和使用環境等條件選用。焊條的熔敷金屬的主要化學成分應與母材的主要成分想接近，以保證焊接接頭的各項性能與母材相當。但考慮到焊條在電弧中的合金損失，在焊條中還應含有一些其他元素，以改善焊縫性能或焊接工藝性能。
若采用相同成分的焊條達不到設計要求或者沒有合適的類似合金成分的焊條時，則推薦選用性能高一級別的焊條，以保證焊縫的使用性能不低于母材。
（2）鎳及鎳合金焊條的使用注意事項
① 母材的準備：焊前應認真清除母材表面的油污、油漆、灰塵等臟物。
② 為防止氣孔，采用短弧焊接。
③ 采用較小焊接電流，焊前不預熱，保持較低道間溫度（<150℃），以避免母材過熱。
④ 焊接時焊條擺動幅度要小，焊道兩側停留稍長時間，以利氣孔和焊渣的浮出。
⑤ 收弧時注意填充滿弧坑，以免產生弧坑裂紋。
⑥ 鎳及鎳合金的顯微組織為奧氏體，有強的熱裂紋傾向，在焊接角焊縫時，要求焊道呈凸起狀，這樣可以較好地防止熱裂紋的產生。
|
焊條牌號
|
型號
|
電流種類
|
主要用途
|
|
|
SMK-Ni102
|
ENi-0
|
交直流
|
用于化工設備、食品工業，醫療器械制造中鎳基合金和雙金屬的焊接，也可用作異種金屬的過渡層焊條，具有良好的熔合性和抗裂性。
|
|
|
|
|
SMK-Ni103
|
～
|
直流
|
用于鎳基合金和異種鋼焊接，還可用于焊后不能熱處理的大厚度鐵素體鋼構件的焊接。
|
|
|
|
|
SMK-Ni105
|
～
|
直流
|
用于INCONEL690合金的焊接以及鎳基合金和異種鋼的焊接。
|
|
|
|
|
SMK-Ni112
|
ENi-1
|
交直流
|
用于化工設備、食品工業，醫療器械制造中鎳基合金和雙金屬的焊接，也可用作異種金屬的過渡層焊條，具有良好的熔合性和抗裂性。
|
|
|
|
|
SMK-Ni202
|
ENiCu-7
|
交直流
|
用于鎳銅合金與異種鋼的焊接，也可用作過渡層堆焊材料。
|
|
|
|
|
SMK-Ni207
|
ENiCu-7
|
直流
|
用于焊接蒙乃爾合金焊條或異種鋼，也可用作過渡層堆焊材料。
|
|
|
|
|
SMK-Ni307
|
ENiCrMo-0
|
直流
|
用于焊接有耐熱、耐蝕要求的鎳基合金，也可用于一些難焊合金、異種鋼的焊接及堆焊。
|
|
|
|
|
SMK-Ni307A
|
ENiCrFe-3
|
直流
|
用于焊接有耐熱、耐蝕要求的鎳基合金，如因康鎳600、601等，也可用于一些難焊合金、異種鋼的焊接及堆焊。
|
|
|
|
|
SMK-Ni307B
|
ENiCrFe-3
|
直流
|
用于焊接有耐熱、耐蝕要求的鎳基合金，如因康鎳600、601等，也可用于異種鋼的焊接或耐蝕堆焊材料。
|
|
|
|
|
SMK-Ni307-1
|
ENiCrFe-1
|
直流
|
用于鎳鉻鐵合金（UNS N06600、UNSN06601)的焊接及鋼的堆焊。具有良好的異種金屬焊接性能。也可以在工作溫度980°時應用，但溫度高于820°時，抗氧化性和強度下降。
|
|
|
|
|
SMK-Ni307-2
|
ENiCrFe-2
|
直流
|
用于鎳鉻鐵合金（如 UNS N08800、UNSN06600)的焊接，特別適用于異種金屬的焊接、過渡層焊接及堆焊，也可以在工作溫度980°時應用，但溫度高于820°時，抗氧化性和強度下降。
|
|
|
|
|
SMK-Ni307-3
|
ENiCrFe-3
|
直流
|
用于鎳鉻鐵合金（如 UNS N06600)的焊接及鋼的堆焊，工作溫度一般不高于480°，抗裂性好。適合原子爐壓力容器及化學槽焊接。
|
|
|
|
|
SMK-Ni307-4
|
ENiCrFe-4
|
直流
|
用于鎳鉻鐵合金的焊接，如Ni600、Ni800/800H及類似或工作溫度900°的鎳基高溫合金，也可用于含Ni3%-9%的低溫鋼，如ASTM A333、A334、A353、A522、A553的焊接，還可用于Mo400、Ni825與不銹鋼、低合金鋼之間的異種金屬焊接。
|
|
|
|
|
SMK-Ni307-7
|
ENiCrFe-7
|
直流
|
用于核工程、硫酸、硝酸及氫氟制造裝置上，如鎳690合金、ASTM B167、B166、B168等，也可用于鎳鉻鐵與不銹鋼的焊接和在鋼上堆焊耐蝕層。
|
|
|
|
|
SMK-Ni317
|
～
|
直流
|
用于焊接鎳基合金及鉻鎳奧氏體鋼，也可用于異種鋼焊接。
|
|
|
|
|
SMK-Ni327
|
ENiCrMo-0
ENiCrFe-9
|
直流
|
用于焊接有耐熱、耐蝕要求的鎳基合金，也可用于一些難焊合金、異種鋼的焊接及堆焊。
|
|
|
|
|
SMK-Ni327-3
|
ENiCrMo-3
|
直流
|
用于鎳鉻鉬合金的焊接，特別是 UNSN06625 類合金與其它鋼種以及鎳鉻鉬合金復合鋼的焊接和堆焊，也可用于低溫條件下的 Ni9% 鋼焊接。
|
|
|
|
|
SMK-Ni327-4
|
ENiCrMo-4
|
直流
|
用于低碳鎳鉻鉬合金的焊接，如哈氏合金C276、ASTM B574 B575 B619 B622 B626,也可用于與其它鎳基合金的異種鋼焊接。
|
|
|
|
|
SMK-Ni327-6
|
ENiCrMo-6
|
直流
|
用于 Ni9% 鋼的焊接，也可用于異種鋼及難焊合金的焊接。
|
|
|
|
|
SMK-Ni327-8
|
ENiCrMo-8
|
直流
|
用于鎳鉬合金和 9% Ni鋼的焊接。
|
|
|
|
|
SMK-Ni327-13
|
ENiCrMo-13
|
直流
|
用于鎳鉻鉬合金如 ASTM B574、B575、B619、B622、B626 等的焊接，也可用于鎳鉻鉬合金與其它合金的焊接。
|
|
|
|
|
SMK-Ni337
|
ENiCrMo-0
|
直流
|
用于核反應堆壓力容器密封面堆焊及塔內構件焊接，也可用于復合鋼、異種鋼以及相同類型的鎳基合金焊接。
|
|
|
|
|
SMK-Ni347
|
ENiCrFe-0
|
直流
|
用于核電站穩壓器、蒸發器管板接頭的焊接，也可用于復合鋼、異種鋼以及相同類型的鎳基合金焊接。
|
|
|
|
|
SMK-Ni357
|
ENiCrFe-2
|
直流
|
用于焊接有耐熱、耐蝕要求的鎳基合金，也可用于異種鋼的焊接或用作過渡層及堆焊焊條。
|
|
|
|
詳細說明
詳細說明
合金焊絲的選用和使用
（1）鎳及鎳合金焊絲的選用原則 鎳及鎳合金焊條主要根據被焊母材的合**號、化學成分和使用環境等條件選用。焊條的熔敷金屬的主要化學成分應與母材的主要成分想接近，以保證焊接接頭的各項性能與母材相當。但考慮到焊條在電弧中的合金損失，在焊條中還應含有一些其他元素，以改善焊縫性能或焊接工藝性能。
若采用相同成分的焊條達不到設計要求或者沒有合適的類似合金成分的焊條時，則推薦選用性能高一級別的焊條，以保證焊縫的使用性能不低于母材。
（2）鎳及鎳合金焊絲的使用注意事項
① 母材的準備：焊前應認真清除母材表面的油污、油漆、灰塵等臟物。
② 為防止氣孔，采用短弧焊接。
③ 采用較小焊接電流，焊前不預熱，保持較低道間溫度（<150℃），以避免母材過熱。
④ 焊接時焊條擺動幅度要小，焊道兩側停留稍長時間，以利氣孔和焊渣的浮出。
⑤ 收弧時注意填充滿弧坑，以免產生弧坑裂紋。
⑥ 鎳及鎳合金的顯微組織為奧氏體，有強的熱裂紋傾向，在焊接角焊縫時，要求焊道呈凸起狀，這樣可以較好地防止熱裂紋的產生。
|
型號
|
特性/用途
|
|
|
|
|
ERNi-1
Ni2061
|
焊接 200 、 201 鎳合金以及鍍鎳鋼板； - 鋼與鎳異種材料的焊接；- 鋼的表面堆焊。
|
|
|
|
|
ERNiCu-7
Ni4060
|
- 蒙乃爾 400 合金自身的焊接；以及蒙乃爾 400 合金與鋼的焊接； -用于鋼的表面堆焊。
|
|
|
|
|
ERNiCr-3
Ni6082
|
用于鎳鉻合金、鎳鉻鐵合金、鎳鐵鉻合金的焊接，也可用于渡層與異種金屬接頭的焊接和低溫條件下鎳鋼的焊接。
|
|
|
|
|
ERNiCrFe-5
Ni6062
|
用于鎳鐵鉻合金、鎳鉻鐵的焊接以及特殊用途的異種金屬焊接。
|
|
|
|
|
ERNiCrFe-7
Ni6052
|
用于高鉻鎳基合金的焊接，也可用于低合金和不銹鋼以及異種金屬的耐腐蝕層的堆焊。主要應用于核電工程。
|
|
|
|
|
ERNiCrFe-7A
|
用于高鉻鎳基合金的焊接，也可用于低合金和不銹鋼以及異種金屬的耐腐蝕層的堆焊。主要應用于核電工程。
|
|
|
|
|
ERNiFeCr-1
Ni8065
|
用于鉻鎳鉬銅合金、鎳鐵鉻鉬合金的焊接，也可用于鋼材表面堆焊和鎘離層堆焊。
|
|
|
|
|
ERNiCrMo-4
Ni6276
|
INCO-WELD C276 及其它 Ni-Cr-Mo 耐腐蝕合金的焊接； - 表面堆焊合金鋼的焊接、鋼的表面堆焊
|
|
|
|
|
ERNiCrMo-7
Ni6455
|
用于鎳基、鐵鎳基合金及不銹鋼等的焊接，也可用于鎳基與鐵鎳基或不銹鋼、鎳基與不銹鋼與低合金鋼異種材料的焊接與堆焊。
|
|
|
|
|
ERNiCrMo-3
Ni6625
|
INCONEL625 、 INCONEL825 、 INCONEL25-6Mo 以及MONEL400 合金的焊接； - 超高強度奧氏體鋼與 INCOLOY020 合金之間的焊接； - 鎳基合金與不銹鋼異種材料間的焊接； - 鋼的堆焊。
|
|
|
|
|
ERNiCrMo-14
Ni6686
|
INCONEL686 及其它 Ni-Cr-Mo 合金的焊接； - 表面堆焊合金鋼、雙相鋼、超高強度雙相鋼、超高強度奧氏體不銹鋼的焊接； - 鋼的表面堆焊。
|
|
|
|
|
ERNiCoCrMo-1
Ni6617
|
用于低碳鎳鈷鉬合金的焊接和鋼表面堆焊，也可用于異種高溫合金和鑄造高鎳合金的焊接。
|
|
|
|
|
ERCuNi
|
用于銅鎳合金以及特定的青銅材料自身的焊接，以及這些材料和蒙乃爾 400 合金或 Nickel200 之間的焊接。
|
|
|
|
|
ERNiCrFe-3
|
抗蠕變接頭的焊接、異種材料焊接； - 奧氏體、鐵素體鋼和高鎳合金的焊接、含鎳 9% 合金鋼焊接
|
|
|
|
|
ERNiCrMo-10
|
INCONEL622 及其它 Ni-Cr-Mo 耐腐蝕合金的焊接； - 表面堆焊合金鋼、雙相鋼、超高強度雙相鋼、超高強度奧氏體不銹鋼的焊接； -鋼的表面堆焊。
|
|
|
|
詳細說明
詳細說明
|
Category
類 別
|
Trade-
mark
牌 號
|
Chemical
composition
化學成份(%)
|
Hardness
硬 度
|
Application
用 途
|
|
Oxy-
Acetylene
Flame
spray-
using
氧
乙
炔
焰
噴
焊
|
F103
|
Cr10 B1.5 Si3 Ni Rem.
|
HRc 25
|
Spray-fusing of cast iron
parts, such as die for glass, cylinder, and guide.
鑄鐵件的噴焊，如玻璃模具，汽缸、導軌
|
|
F101
|
Cr10 B2.5 Si3 Ni Rem.
|
HRc 45
|
Spray-fusing of parts
resistance to wear and corrosion, such as valve, the rotator and piston of
pump.
耐磨、耐蝕件的噴焊，如閥門、泵轉子、泵柱塞
|
|
F101Fe
|
Cr10 B2.5 Si3 Fe10
Ni Rem.
|
HRc 45
|
Spray-fusing of corrosion-resistant
parts, such as axle and stigma.
耐磨件的噴焊，如軸類、汽門
|
|
F102
|
Cr16 B4 Si4 Ni Rem.
|
HRc 60
|
Spray-fusing of parts
resistance to wear, corrosion and high temperature oxidation, such as die and
piston.
耐磨、耐蝕、抗高溫氧化工件的噴焊，如模具、柱塞
|
|
F102Fe
|
Cr16 B4 Si4 Fe15
Ni Rem.
|
HRc 60
|
Spray-fusing of
corrosion-resistant parts, such as axle and cold die.
耐磨件的噴焊，如軸類、冷模具
|
|
F105
|
F102+50%WC
|
HRc 60
|
Spray-fusing of parts
resistance to grain-wear , such as guide plate, scraper and blade of fan.
抗磨粒磨損場合的噴焊，如導板、刮板、風機葉片
|
|
F105Fe
|
F102Fe+35%WC
|
HRc 60
|
Spray-fusing of parts
resistance to grain-wear, such as guide plate, scraper and blade of fan.
抗磨粒磨損場合的噴焊，如導板、刮板、風機葉片
|
|
F108
|
F102+80%WC
|
HRc 60
|
Spray-fusing of parts
resistance to strong grain-wear and free machining, such as harrow teeth of
dredger.
抗強烈磨粒磨損，無需加工場合的噴焊，如挖泥船耙齒
|
|
F301
|
Cr5 B4 Si4 Ni30
Fe Rem.
|
HRc 45
|
Spray-fusing of vulnerable
parts of agricultural machinery and mining machinery, such as gear and
axletree.
農機,礦山機械易損件的噴焊，如齒輪，車軸
|
|
Track iron powder
軌鐵粉
|
Cr5 B1.5 Si3 Ni30
Fe Rem.
|
HRc 28
|
Repair spray-fusing of
defects such as scratch and concavity of railroad track.
鐵路鋼軌擦傷、低塌等缺陷的修復噴焊
|
|
Oxy-acetylene flame spraying
氧
乙
炔
焰
噴
涂
|
F111
|
Cr5 B1.5 Si3 Ni30
Fe Rem.
|
HB 150
|
Spraying of bearing and
cutting parts etc.
軸承、切削件等的噴涂
|
|
F113
|
Cr10 B1.5 Si3 Ni Rem.
|
HB 250
|
Spray-fusing or spraying,
such as roll, piston and axle of wear and corrosion resistance.
噴涂亦可噴焊，如滾筒、柱塞、耐蝕耐磨軸等
|
|
F313
|
Cr15 B1.5 Fe Rem.
|
HB 250
|
Spraying of dryer of
papermaking and axle.
造紙烘缸、軸類的噴涂
|
|
F314
|
Cr18 Ni9 B1.5 Fe Rem.
|
HB 250
|
Spraying of axle.
軸類噴涂
|
|
F412
|
Sn10 P0.3 Cu Rem.
|
HB 80
|
Spraying of axle and
bearing.
軸、軸承的噴涂
|
|
F512
|
復合Al5Ni95
|
|
Backing spray of transition
layer between base and working layer.
噴涂層的基體與工作層之間過渡（打底）層用噴涂
|
|
PTA
hardfacing
等
離
子
弧
噴
焊
|
F221
|
Cr26 W5 B0.7 Co Rem.
|
HRc 43
|
PTA hardfacing of sealing
surface of high temperature and high pressure valve and the edge of hot
shearing tool.
高溫高壓閥門密封面、熱剪切刃口的等離子噴焊
|
|
F223
|
Cr21 W5 B1.5 Co Rem.
|
HRc 40
|
PTA hardfacing of parts
resistance to wear and corrosion at high temperature, such as valve under
high temperature and high pressure, and blower.
高溫下耐磨耐蝕件的噴焊，如高溫高壓閥門、鼓風機
|
|
F321
|
Cr13 B1.5 Si1 Fe Rem.
|
HRc 45
|
PTA hardfacing of
corrosion-resistant parts under mid-temperature and mid-pressure, such as
stop-plate etc.
中溫中壓閥門的閘板及其他耐磨件的等離子噴焊
|
|
F322
|
Cr23 Ni13 Si5 B1
Fe Rem.
|
HRc 40
|
PTA hardfacing of
corrosion-resistant parts under mid-temperature and mid-pressure, such as
valve base etc.
中溫中壓閥門的閥座及其他耐磨件的等離子噴焊
|
|
F422
|
Sn10 P0.3 Cu Rem.
|
HB 80
|
PTA hardfacing of axle and
bearing etc.
軸、軸承等離子噴焊
|
|
Category
類 別
|
Trade-
mark
牌 號
|
Chemical
composition
化學成份(%)
|
Hardness
硬 度
|
Application
用 途
|
|
Oxy-
Acetylene
Flame
spray-
using
氧
乙
炔
焰
噴
焊
|
F103
|
Cr10 B1.5 Si3 Ni Rem.
|
HRc 25
|
Spray-fusing of cast iron
parts, such as die for glass, cylinder, and guide.
鑄鐵件的噴焊，如玻璃模具，汽缸、導軌
|
|
F101
|
Cr10 B2.5 Si3 Ni Rem.
|
HRc 45
|
Spray-fusing of parts
resistance to wear and corrosion, such as valve, the rotator and piston of
pump.
耐磨、耐蝕件的噴焊，如閥門、泵轉子、泵柱塞
|
|
F101Fe
|
Cr10 B2.5 Si3 Fe10
Ni Rem.
|
HRc 45
|
Spray-fusing of
corrosion-resistant parts, such as axle and stigma.
耐磨件的噴焊，如軸類、汽門
|
|
F102
|
Cr16 B4 Si4 Ni Rem.
|
HRc 60
|
Spray-fusing of parts
resistance to wear, corrosion and high temperature oxidation, such as die and
piston.
耐磨、耐蝕、抗高溫氧化工件的噴焊，如模具、柱塞
|
|
F102Fe
|
Cr16 B4 Si4 Fe15
Ni Rem.
|
HRc 60
|
Spray-fusing of
corrosion-resistant parts, such as axle and cold die.
耐磨件的噴焊，如軸類、冷模具
|
|
F105
|
F102+50%WC
|
HRc 60
|
Spray-fusing of parts
resistance to grain-wear , such as guide plate, scraper and blade of fan.
抗磨粒磨損場合的噴焊，如導板、刮板、風機葉片
|
|
F105Fe
|
F102Fe+35%WC
|
HRc 60
|
Spray-fusing of parts
resistance to grain-wear, such as guide plate, scraper and blade of fan.
抗磨粒磨損場合的噴焊，如導板、刮板、風機葉片
|
|
F108
|
F102+80%WC
|
HRc 60
|
Spray-fusing of parts
resistance to strong grain-wear and free machining, such as harrow teeth of
dredger.
抗強烈磨粒磨損，無需加工場合的噴焊，如挖泥船耙齒
|
|
F301
|
Cr5 B4 Si4 Ni30
Fe Rem.
|
HRc 45
|
Spray-fusing of vulnerable
parts of agricultural machinery and mining machinery, such as gear and
axletree.
農機,礦山機械易損件的噴焊，如齒輪，車軸
|
|
Track iron powder
軌鐵粉
|
Cr5 B1.5 Si3 Ni30
Fe Rem.
|
HRc 28
|
Repair spray-fusing of defects
such as scratch and concavity of railroad track.
鐵路鋼軌擦傷、低塌等缺陷的修復噴焊
|
|
Oxy-acetylene flame spraying
氧
乙
炔
焰
噴
涂
|
F111
|
Cr5 B1.5 Si3 Ni30
Fe Rem.
|
HB 150
|
Spraying of bearing and
cutting parts etc.
軸承、切削件等的噴涂
|
|
F113
|
Cr10 B1.5 Si3 Ni Rem.
|
HB 250
|
Spray-fusing or spraying,
such as roll, piston and axle of wear and corrosion resistance.
噴涂亦可噴焊，如滾筒、柱塞、耐蝕耐磨軸等
|
|
F313
|
Cr15 B1.5 Fe Rem.
|
HB 250
|
Spraying of dryer of
papermaking and axle.
造紙烘缸、軸類的噴涂
|
|
F314
|
Cr18 Ni9 B1.5 Fe Rem.
|
HB 250
|
Spraying of axle.
軸類噴涂
|
|
F412
|
Sn10 P0.3 Cu Rem.
|
HB 80
|
Spraying of axle and
bearing.
軸、軸承的噴涂
|
|
F512
|
復合Al5Ni95
|
|
Backing spray of transition
layer between base and working layer.
噴涂層的基體與工作層之間過渡（打底）層用噴涂
|
|
PTA
hardfacing
等
離
子
弧
噴
焊
|
F221
|
Cr26 W5 B0.7 Co Rem.
|
HRc 43
|
PTA hardfacing of sealing
surface of high temperature and high pressure valve and the edge of hot
shearing tool.
高溫高壓閥門密封面、熱剪切刃口的等離子噴焊
|
|
F223
|
Cr21 W5 B1.5 Co Rem.
|
HRc 40
|
PTA hardfacing of parts
resistance to wear and corrosion at high temperature, such as valve under
high temperature and high pressure, and blower.
高溫下耐磨耐蝕件的噴焊，如高溫高壓閥門、鼓風機
|
|
F321
|
Cr13 B1.5 Si1 Fe Rem.
|
HRc 45
|
PTA hardfacing of
corrosion-resistant parts under mid-temperature and mid-pressure, such as
stop-plate etc.
中溫中壓閥門的閘板及其他耐磨件的等離子噴焊
|
|
F322
|
Cr23 Ni13 Si5 B1
Fe Rem.
|
HRc 40
|
PTA hardfacing of
corrosion-resistant parts under mid-temperature and mid-pressure, such as
valve base etc.
中溫中壓閥門的閥座及其他耐磨件的等離子噴焊
|
|
F422
|
Sn10 P0.3 Cu Rem.
|
HB 80
|
PTA hardfacing of axle and
bearing etc.
軸、軸承等離子噴焊
|